Coated Rod for High-Tension Steel LB-62
Référence pièce
Vous pouvez trouver ici le numéro
de référence lié au produit recherché.
LB-62-5-20
Référence pièce
|
|---|
| LB-62-5-20 |
| Référence pièce |
Prix unitaire standard
| Quantité minimale de commande | Remise sur volume | Pole diameter (mm) | Current range, lower (A) | Current range, vertical position, elevating, upper | |
|---|---|---|---|---|---|---|---|
198.19 € | 1 | 8 jours | 5 | 180～240 | 150~200 |
Loading...
Informations de base
| Product Type | Baguette de soudage | Pole length(mm) | 400 | JIS Standard | Z3211 E6216-N1M1 U |
|---|---|---|---|---|---|
| AWS Standard | A5.5 E9016-G Applicable | Compatible Material Type | Rod exemplifies its class, barely hygroscopic | Amount Of Content | 1 Box (5 kg x 4 Boxes) |
| Mass(g) | 20000 | Application and Usage Characteristic | Pressure vessel, bridge, vehicle, and machine welding. Corresponds to 550 to 610 MPa grade steel. Extremely low hydrogen bar, with Nada moisture absorption. Arc concentration, beaded outward appearance is good, and general stance welding is easy. | Main Points of Work | Dry for approximately 1 hour at 350-400°C prior to use. Arc strike portion can cause cracks on base metal. Please use a backtracking or scrap metal method. Although type of steel and plate thickness varies, preheat at 50-100°C. Please note that if a large amount of deposit metal is used in high input heat welding, the strength and durability of the deposit will be reduced. |
| Chemical Composition of Deposited Metal C(%) | 0.06 | Chemical Composition of Deposited Metal Si(%) | 0.66 | Chemical Composition of Deposited Metal Mn(%) | 1.04 |
| Chemical Composition of Deposited Metal Mo(%) | 0.26 | Chemical Composition of Deposited Metal P(%) | 0.011 | Chemical Composition of Deposited Metal S(%) | 0.005 |
| Ni(%) | 0.61 | Identification Color, Rod End Color | Blue White | Identification Color, Secondary Color | Yellow |
| Mechanical Properties of Weld Metal Proof Stress MPa | 550 | Mechanical Properties of Weld Metal Proof Stress, Tensile Strength MPa | 650 | Mechanical Properties of Weld Metal Proof Stress, Elongation(%) | 25 |
| Mechanical Properties of Weld Metal Proof Stress, Absorption Energy(J) | 150(-20℃) | Authorized by the Classification Society of Japan | NK,ABS,LR,CR |
Configurer
Propriétés de base
-
Pole diameter(mm)
-
Current range, vertical position, elevating, upper
-
Type
- LB-62
-
Current range, lower(A)
Filtrer par jours d'expédition standard
-
- Tous les articles
- 8 jours ou moins
Propriétés optionnelles
- Les spécifications et les dimensions de certaines pièces peuvent ne pas être intégralement indiquées. Pour plus de détails, reportez-vous aux catalogues des fabricants .
Assistance technique
Mode de paiement
Fabrication à la demande
Certificats
Copyright © MISUMI Corporation All Rights Reserved.